Sebopeho sa Lik'hemik'hale
Alloy C2000 sebopeho sa lik'hemik'hale
Sebopeho sa lik'hemik'hale tsa Hastelloy C-2000 se bontšitsoe tafoleng e ka tlase:
| Element | Min % | Boholo % |
|---|---|---|
| Cr | 22.00 | 24.00 |
| Mo | 15.00 | 17.00 |
| Fe | - | 3.00 |
| C | - | 0.01 |
| Si | - | 0.08 |
| Co | - | 2.00 |
| Mn | - | 0.50 |
| P | - | 0.025 |
| S | - | 0.01 |
| Cu | 1.30 | 1.90 |
| Al | - | 0.50 |
| Ni | bal |
Lintlha tsa Alloy
Hastelloy C-2000 density, melting point, coefficient of expandity, le modulus of elasticity e bontšitsoe tafoleng e ka tlase:
| Botenya | Melting Point | Coefficient of Katoloso | Modulus of Rigidity | Modulus ea Elasticity |
|---|---|---|---|---|
| 8.5g/cm³ | 1399 °C | 12.4 μm/m °C (20 - 100 °C) | 79 kN/mm² | 206 kN/mm² |
| 0.307 lb/in³ | 2550 °F | 6.9 x 10-6ka/ka °F (70 – 212 °F) | 11458 ksi | 29878 ksi |
Phekolo ea mocheso ea likarolo tse felileng
Alloy C2000 sebopeho sa lik'hemik'hale
Kalafo e tloaelehileng ea mocheso ea Hastelloy C-2000:
| Boemo joalo ka ha bo fanoe ke AWI | Mofuta | Mocheso | Nako | Ho phodisa |
|---|---|---|---|---|
| Anealed kapa Spring Temper | Fokotsa Khatello | 400 - 450 °C (750 - 840 °F) | 2 Hr | Moea |
Thepa
Mehaho e tloaelehileng ea mochini oa Hastelloy C-2000:
| Annealed | ||
|---|---|---|
| Hoo e ka bang.matla a tšepe | <1000 N/mm² | <145 lik'hilograma |
| Hoo e ka bang.mocheso o sebetsang ho itšetlehile ka mojaro ** le tikoloho | -200 ho +400 °C | -330 ho ea ho +750 °F |
| Mohatsela oa Selemo | ||
|---|---|---|
| Hoo e ka bang.matla a tšepe | 1300 - 1600 N/mm² | 189 - 232 ksi |
| Hoo e ka bang.mocheso o sebetsang ho itšetlehile ka mojaro ** le tikoloho | -200 ho +400 °C | -330 ho ea ho +750 °F |